Product Description Introduction epoxy grout including A (etc.), B (curing agent), C (aggregate filler, etc.) three components, but also to adjust the recipe depending on usage, process improvements, in order to meet the different requirements or highlight certain part of the performance. When the routine use, the components can be carried out completely mixed grout operation. If the application temperature is below 15 degrees, you can also construction, but the intensity up slowly, usually three days can be reached. Does not affect the final performance. 1. Product Features (1) high-strength early strength cement-based materials have superior compressive mechanical properties, adhesion, etc., higher early strength. (2) ensure that no shrink grout layer after final shaping full contact with the bearing surface to ensure high accuracy device installed. (3) creep at -40 ℃ to + 80 ℃ alternately freezing and thawing, pressure vibration in harsh physical conditions of long-term use without plastic deformation. (4) High toughness can be resolved by moving the device to deliver the cement-based grout layer may burst dynamic load. (5) corrosion can withstand acid, alkali, salt, oil and other chemicals, long-term exposure to corrosion. 2. Product properties (standard curing conditions: 25 ℃, relative humidity of 50%, maintenance than 7 days) (1) specific gravity (density) of 1.2 to 2.0, the conventional value 1.8 g / cm3, depending on the recipe, with filler and aggregate content was positively correlated relationship, (2) the appearance of conventional curing product as a tan solid, other colors can also be customized, with a smooth flat surface exposed highlights. (3) applicable period (25 ℃) 1 ~ 2 hours with stirring pouring a positive correlation. (4) exothermic peak 30 ℃ ~ 70 ℃, negative correlation with filler and aggregate content in a generally. (5) pressure creep (25 ℃) compression state, within six months of <1.0 × 10-3mm / mm. (6) Thermal expansion coefficient (0 ℃ ~ 60 ℃) completely curing (greater than 7 days) between 10 ~ 50 × 10-6mm / mm / ℃. . Security, non-toxic non-volatile formula, on the environment and human friendly, but the individual who has a slight irritation of the skin should avoid prolonged contact with the skin, should be used to protect and maintain the environment necessary wear ventilation should promptly contact with the skin wash, such as splashing into eyes rinse immediately with plenty of water and, if ingested orally, please drink immediately induce vomiting and seek medical treatment. 4. Packaging and storage of conventional liquid components used iron or plastic barrels, solid components using plastic or paper-plastic bag, also can be customized. Should meet the general chemical cool, dry, airtight, ventilated storage conditions, because the chemical nature of the stability of the product under normal conditions can be stored for at least one year, after the test can still be used by the overdue harmless. 1. epoxy grout construction program contact the epoxy grout surface pretreatment of the concrete surface shall be chiseled surface laitance and expose its solid grassroots ensure grout surface is clean, dry and free of grease. Concrete joints grind 25mm thick outer edge chamfered edges to increase the edge of the grout and adhesive base area to be bonded should be no corrosion of metal surfaces (up to SSPC, SP6 finish requirements). 2. Construction of the temperature and ambient air temperatures, including concrete foundations, in order to obtain the best working condition, must be left for 24 hours at 15-25 ° C environment before grouting, construction and subsequent control of the ambient temperature within 15- 24 hours 32 ° C, 20 ° C is most appropriate. Summer construction to avoid the midday heat, when necessary, to build awnings; winter when the temperature is low, you should build greenhouses heated in filling area to ensure environmental temperature greater than 15 ° C, the construction should choose noon. 3. The hand-held mixing stirrer (200-250rpm) mixed A (resin), B (hardener) for about 3 minutes; 2, (15-20rpm) was added C (filler) in a low speed mixer to make with high-power A, B blended mixture, stir until all invasive orthopedics that is completed in about 5-10 minutes; at low temperatures in order to ensure the flow of the mixture may be appropriate to reduce C (filler) used. 4. epoxy grout grout should be filling one side to the other side; grouting process can squeeze shock but do not stir to avoid air entrapment inclusion therein; grouting distance is greater than 1.5m, you should use a high filling funnel method, using gravity Principle auxiliary pressure grouting. Grouting work must be completed as soon as possible in a row. Single grout layer thickness control in 25mm to 35mm between; a single bolt hole filling depth is less than 1500mm; foam board required reserve strip joints on the basis of surface Sticky grouting volume exceeding 1.8m × 1.8m × 150mm, filling the final setting After its surface portion cut out, and then sealed with epoxy sealed making permanent limb joints. 5. Check dense: After filling, the substrate with a hammer percussion equipment: If issued tinkle indicates dense grout layer, such as issuing thunderous sound indicates that the grout layer hollowing. 6. Surface collection of light and form removal: After the grout and epoxy grout before the initial setting, to achieve the aesthetic effect, the exposed surface of the received light gray knife; after the final setting, you can form removal. The above data for reference only, please be sure to test the relative performance before use. Have any questions please contact our technical staff to resolve.